Texture and mechanical properties of duplex stainless steel through symmetric hot rolling

Texture et propriétés mécaniques d’un acier inoxydable duplex obtenu par laminage à chaud symétrique

Sezione Materiali per Applicazioni Meccaniche, Dipartimento di Meccanica – Politecnico di Milano, Via La Masa 34, 20156 Milano, Italy

Received: 12 January 2010
Accepted: 25 May 2010

Abstract

Experimental rolling trials were performed at different temperatures on EN 1.4462 duplex steel imposing also different reduction ratios and a possible solution quenching. A clear and significant relation between the applied thermo-mechanical process and the microstructural evolution was shown, and it is useful for designing the steel microstructure. The mechanical properties, the micro-structural features and the texture characteristics were defined for each condition in order to point out the operative parameters (i.e. thermal level, imposed strains and application of solution quenching) that permit to maximize the formability of the final hot-rolled products.

Résumé

Des expériences de laminage à chaud symétrique ont été réalisées à différentes températures sur un acier duplex EN 1.4462, en imposant différents taux de réduction, suivies par un éventuel recuit. Une relation claire et significative a été démontrée entre le process thermomécanique appliqué et l’évolution micro-structurale, permettant une optimisation de la microstructure de l’acier. Les propriétés mécaniques, les caractéristiques microstructurales et de texture ont été définies pour toutes les conditions afin de trouver les paramètres opérationnels (température, déformation imposée et application d’un éventuel recuit et d’une trempe), qui permettent de donner la formabilité maximale aux produits finis après laminage à chaud.