Identification du comportement thermomécanique d’un alliage CuCr1Zr^*

¹ LIMatB, Université de Bretagne-Sud / UEB, Centre de Recherche Ch. Huygens, Rue de Saint-Maudé, BP 92116, 56321 Lorient Cedex, France
e-mail: denis.carron@univ-ubs.fr
² CEA, DEN, DM2S, SEMT, LTA, 91191 Gif-sur-Yvette, France

Received: 2 February 2011
Accepted: 1 March 2011

Abstract

The mechanical properties of a CuCr1Zr alloy were measured with the help of a Gleeble 3500 machine at temperatures ranging from 250 °C to 1000 °C. Some tensile tests were also performed at 20 °C. The measured data were first used to determine the thermal linear coefficient at different temperatures. The measured curves were then simulated with an elasto-visco-plastic constitutive model assuming that the material behaviour was isotropic. This law requires the knowledge of temperature dependent parameters that were determined by inverse method. This work represents a part of a PhD study on hot tearing susceptibility during welding.

Résumé

Des essais thermomécaniques sur machine Gleeble 3500 ont été réalisés entre 250 °C et 1000 °C afin de caractériser le comportement à chaud d’un alliage CuCr1Zr. En complément, des essais de traction à température ambiante ont été effectués. Les données recueillies sont utilisées tout d’abord pour caractériser la dilatation thermique de cet alliage. On identifie ensuite, par méthode inverse, les paramètres d’une loi de comportement élasto-viscoplastique à écrouissage isotrope. La dépendance des paramètres avec la température a aussi été identifiée. Cette étude s’est inscrite dans le cadre d’une thèse de doctorat sur la fissuration à chaud en soudage.