Influence of B2O3 on viscosity and structure of low MgO slag containing titanium
School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing,
Beijing
100083, PR China
* email: m18811345752@163.com
Received:
9
September
2017
Accepted:
15
December
2017
The viscous behavior of CaO–SiO2–15.2 wt% Al2O3–4.8 wt% MgO–TiO2–B2O3 slags is studied. The effect of the TiO2 and B2O3 on the viscosity and apparent activation energy, as well as the effect of B2O3 on structure is investigated through Raman spectroscopy. The viscosity and apparent activation energy of CaO–SiO2–15.2 wt% Al2O3–4.8 wt% MgO–TiO2 are decreased with increased TiO2 content, which can be explained by the network modifier role that TiO2 acts in slags. The addition of B2O3 can reduce the viscosity of CaO–SiO2–15.2 wt% Al2O3–4.8 wt% MgO–TiO2–B2O3 slags, and it brings about a turning point on apparent activation energy curves. Raman spectroscopy shows that B2O3 acts as acidic oxide and increases the degree of polymerization of slags. However, with the addition of B2O3, the appearance of two dimensional [BO3] structure units and the low strength energy of B–O bonds can reduce the viscous resistance in molten slags and decrease the viscosity.
Key words: Low MgO / TiO2 / B2O3 / Raman
© EDP Sciences, 2018
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.