Degradation behaviors of coke under complex solution loss conditions
1
Jitang College, North China University of Science and Technology,
Tangshan,
Hebei
063210, PR China
2
College of Chemical Engineering, North China University of Science and Technology,
Tangshan,
Hebei
063210, PR China
* e-mail: raykuo@126.com
Received:
24
April
2020
Accepted:
2
November
2020
Solution loss reaction of coke provides reducing agent for ironmaking, which is an important chemical reaction in blast furnace. The coke itself is also degraded by the loss of carbon. In this paper, the degradation behavior of coke under complex conditions including alkali metal enrichment, simulated blast furnace temperature and atmosphere was studied. The pore size and pore wall thickness distribution of coke were measured by a microscope to characterize the structure of coke. The gasification reaction rate of coke matrix was measured by a thermogravimetric analyzer to characterize the matrix reactivity of coke. The results show that a coke has high CRI and low CSR, but it has high matrix reactivity and thick pore wall, which may lead higher strength after solution loss under alkali metal enrichment and simulated blast furnace atmosphere and heating conditions.
Key words: coke / solution loss / post-reaction strength / pore structure
© EDP Sciences, 2020
Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.
Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.
Initial download of the metrics may take a while.